EFFECT OF COOLING RATE DURING SOLIDIFICATION ON THE HARD PHASES OF M23C6-TYPE OF CAST CoCrMo ALLOY

Autor

MELVYN ALVAREZ VERA

ALEJANDRA HERNANDEZ RODRIGUEZ

Nivel de Acceso

Acceso Abierto

Licencia

http://creativecommons.org/licenses/by-nc-nd/4.0

Materias

efecto de la tasa de enfriamiento en la solidificación de aleaciones de aluminio - (ARTÍCULO) INGENIERÍA Y TECNOLOGÍA - (CTI) CIENCIAS TECNOLÓGICAS - (CTI)

Resumen o descripción

Microstructural morphology of CoCrMo alloy by control of the cooling rate during the solidification was investigated.

Samples were obtained using both an induction furnace for slow cooling rate and electric arc furnace for fast

cooling rate. Microstructural characterizations were performed with metallographic techniques. It was found that

the difference between the formation temperature of hard secondary phases of M23C6-type carbides determine the

reduction of carbide size by increasing the cooling rate.

Fecha de publicación

2016

Tipo de publicación

Artículo

Versión de la publicación

Versión publicada

Recurso de información

http://comimsa.repositorioinstitucional.mx/jspui/handle/1022/180

Formato

application/pdf

Fuente

UDC – UDK 669.25.26.28:621.747:66.065:621.56/.59:620.18=111

Idioma

Inglés

Sugerencia de citación

M. ALVAREZ-VERA, A. HERNÁNDEZ-RODRÍGUEZ, M. A. L. HERNÁNDEZ-RODRÍGUEZ, A. JUÁREZ HERNÁNDEZ, J. R. BENAVIDES-TREVIÑO, J. H. GARCÍA-DUARTE (2016). EFFECT OF COOLING RATE DURING SOLIDIFICATION ON THE HARD PHASES OF M23C6-TYPE OF CAST CoCrMo ALLOY. METABK 55(3) 382-384 (2016). ISSN 0543-5846.

Repositorio Orígen

COMIMSA

Descargas

308